So two months later...
The framework is clearly lightened up considerably than previously. Though I do not know why these did not brighten up as much as the ones previously..
- f1.jpg (21.5 KiB) Viewed 2629 times
The button on the left was also just left out in our conservatory with the framework above, however that was in a plastic bag filled with ozone which I mostly remembered to redo once a week.. It did not seem to make any difference at all over the framework was just left out in the open.
The button on the right is the one which had been soaking almost continuously in ozone infested waters... Clearly that one has brightened up considerably more. I also think it is basically the original colour now going by the plastics hook parts.. There is some slight blooming there, could be that the water dried up couple of weeks ago so that was likely the cause..
- b1.jpg (214.38 KiB) Viewed 2629 times
One thing I did just notice is that if we take the bottom of the button as original core, then it would seem there are actually different coloured plastics being used..
So while there is a noticeable difference between the left and right button (likely came from different mice) , the difference on the left button between top and bottom is not actually that much.. It does look like the plastic is discoloured, but I am not really convinced it is discoloured as much as it looks, and it is just the actual colour of the plastic.. So as such, assuming that, the left button almost cleaned up like the original colour.
- b2.jpg (326.22 KiB) Viewed 2629 times
So I think basic conclusion is that if plastic is left in ozone infested waters for over a month, it will lighten up like new.. At least eventually.. After that, if left out in the open, the effect seems to continue where it will lighten up even more on its own..
In terms of sunlight and heat, at least out in the open, it does not seem to really make any difference.. The bottom which was in the ozone water was generally in warm water, because of the warmth in our conservatory, but overall I don't think it was much of a factor..
However going by previous results, the quickest effect was in my ultrasonic cleaner, where it was heated up and ozone was running as well.
So I would say the steps are to keep blasting the ultrasonic cleaner at a high temperature with ozone until the plastics look almost like correct colour. As to if the ultrasonics are running or not I have not experimented, but I did have the cleaner running a lot of the time during the initial treatment. I would assume the ultrasonics don't have much effect overall but I haven't experimented either way. I think the heat is the main factor with the ozone bubbling away in the tank. I think my tank was running around 70C with ozone running on and off during the day (likely actually documented this somewhere one of the above posts).
Then they can be simply left out in the open for another month where they will continue to lighten up. The effect may be speeded up if the plastic is left in soaking in ozone infested water.. But I am not really sure if it would speed things up much.. if anything.
The whole point of this experiment was to lighten up the plastic without using chemicals and to actually obtain the original colour without basically bleaching the plastic. The problem with peroxides is that it actually starts making plastics go white which is not the original colour of the plastics. With this method, the plastic seems to go back to the original colour and does not have the bleaching effect.
Final thoughts ?
Well obviously this process does work incredibly well, however, it is also incredibly slow. But the main advantage here is that it does not bleach the plastic to white and it pretty much uses nothing else but water, heat, and ozone. After initial treatment process seems to continue all by itself.
It would be interesting if a large heated tank could be constructed to enclose a entire case... Heated up to over 70C.. And have a huge ozone generator been continuously via long bubble bars.. Someone else can do that experiment